Титановые аноды с платиновым покрытием для твердого хромирования

For The coating of anodes, UTron has designed a novel high-temperature electrolysis method for platinum coating; it is produced on the anode in molten salt with a platinum content at a temperature of 550°C. It is significantly superior to products coated with platinum in aqueous electrolytes. The purity of the coating is at least 99.9 percent. The ductility, adhesion and corrosion resistance of the platinum coating are considerably better, while the internal stresses are kept to a minimum. The coating thickness distribution is much more uniform, because of the dimensional stability of the anodes.

Parameters of the Platinum plated Titanium Anodes for Hard Chrome Plating:
Substrate: Titanium;
Coating: Platinum;
Coating thickness: 0.5-10µm;
Shape: plate, mesh, cylindrical mesh, wire, rods, tubes, sheets (expanded mesh form is widely used);
Solution: higher chromic acid solution;
Current densities Fluoride content: ~ 10 mg F /L.

Titanium mesh with Platinum plating layer                                          Titanium plate with Platinum plating layer

Titanium rod with Platinum plating layer                                               Titanium tube with Platinum plating layer

Features:
Dimensionally stable;
Constant cell voltage;
Highly conductive;
Good corrosion resistant properties in sulphate solutions;
Reduced electricity consumption;
Lower oxygen overvoltage;
Lighter weight, ease installation and removal;
Shorter downtimes;  
No sludge is formed as the anodes don’t dissolve like lead;
Longer bath life;
Easily fabricated into any shape.

Applications:
PCB Copper Plating;
Cathodic protection;
Jewelry electroplating bath;
Electronics and semiconductor industry;
Precious and non- precious metal electroplating.